Shandong Sinopec Qilu PVC Resin
Visually PVC resin is white amorphous powder with particle size of 60-250um and apparent density 0.40-0.60g/ml. Under normal temperature, 100g resin can absorb 14-27g plasticizer.
QILU brand PVC is produced with the patent technology of Japanese Shinetsu Chemical Company Ltd. and American Oxy Vinyls Company with introduced package equipments. 14 grades of products with different performances and uses can be made by applying the process of suspension polymerization and consuming VCM as its feedstock.
The main grades of QILU brand PVC are: S-700, S-800, S-1000, S-1300, QS-650, QS-800F, QS-850F, QS-1000F, QS-1050P, QS-1200 and QS-1350F.
Grade S-700
Grade S-700 is mainly used to produce transparent flakes, and can be pressed to hard or semi-hard slice or sheet for package, floor material, hard film for lining (for candy wrapping paper or cigarette packing film), etc. It can also be extruded to hard or semi-hard slice, sheet, or irregularly shaped bar for package. Or it can be injected to make joints, valves, electric parts, auto accessories and vessels.
| Grade | PVC S-700 | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 650-750 | GB/T 5761,Appendix A | K value 58-60 | |
| Apparent density, g/ml | 0.52-0.62 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 14 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 0.25mm mesh ≤ | 2.0 | Method 1: GB/T 5761, Appendix B Method2: Q/SH3055.77-2006, Appendix A |
|
| 0.063mm mesh ≥ | 95 | |||
| Fisheye number, No./400cm2, ≤ | 30 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 20 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %, ≥ | 75 | GB/T 15595-95 | ||
Grade S-800
Grade S-800 is mainly used to produce transparent flakes, and can be pressed to hard or semi-hard slice or sheet for package, floor material, hard film for lining (for candy wrapping paper or cigarette packing film), etc. It can also be extruded to hard or semi-hard slice or sheet for package, sheet, or irregularly shaped bar. Or it can be injected to make joints, valves, electric parts, auto accessories and vessels.
| Grade | PVC S-800 | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 750-850 | GB/T 5761,Appendix A | K value 60-62 | |
| Apparent density, g/ml | 0.51-0.61 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 16 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 30 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 20 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %, ≥ | 75 | GB/T 15595-95 | ||
Grade S-1000
Grade S-1000 can be used to produce soft film, sheet, manmade leather, piping, shaped bar, bellow, cable protection piping, packing film, sole and other soft sundry goods.
| Grade | PVC S-1000 | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 970-1070 | GB/T 5761,Appendix A | K value 65-67 | |
| Apparent density, g/ml | 0.48-0.58 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 20 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10minutes later), %, ≥ | 78 | GB/T 15595-95 | ||
Grade S-1300
Grade S-1300 is mainly used to produce high-strength flexible products, pressed materials, rigid and flexible extrusion molding and insulating materials, etc.
| Grade | PVC S-1300 | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 1250-1350 | GB/T 5761,Appendix A | K value 71-73 | |
| Apparent density, g/ml | 0.42-0.52 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 27 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %, ≥ | 78 | GB/T 15595-95 | ||
| Water extracts conductivity, S/cm·g, ≤ | 5 | GB 2915-1999 | ||
Grade QS-650
Grade QS-650 is used for injection molding, pipe fittings, pressed material, rigid foam section, floor material, and extrusion rigid section, etc.
| Grade | PVC QS-650 | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 600-700 | GB/T 5761,Appendix A | K value 57-59 | |
| Apparent density, g/ml | 0.53-0.60 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.40 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 15 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 30 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 20 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %, ≥ | 78 | GB/T 15595-95 | ||
Grade QS-800F
Grade QS-800F is used for extrusion section, wire and cable material, flexible and rigid material, rigid or semi-rigid pressed material, and flexible film and sheet.
| Grade | PVC QS-800F | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 750-850 | GB/T 5761,Appendix A | K value 60-62 | |
| Apparent density, g/ml | 0.51-0.61 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 17 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method2:Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 30 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 20 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %, ≥ | 78 | GB/T 15595-95 | ||
Grade QS-850F
Grade QS-850F is used to produce injection molding, pipe fittings, pressed material, rigid foam section, floor material and extrusion rigid section, etc.,
| Grade | PVC QS-850F | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 800-900 | GB/T 5761,Appendix A | K value 62-64 | |
| Apparent density, g/ml | 0.52 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 20 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | ≥5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %, ≥ | 78 | GB/T 15595-95 | ||
Grade QS-1000F
Grade QS-1000F is used to produce flexible film sheet, pressed material, piping molding-die
tools, wire and cable insulation material, etc..
| Grade | PVC QS-1000F | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 950-1050 | GB/T 5761,Appendix A | K value 65-67 | |
| Apparent density, g/ml | 0.49 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 24 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | ≥5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %,≥ | 80 | GB/T 15595-95 | ||
Grade QS-1050P
Grade QS-1050P is used to produce irrigation pipe, potable water pipe, foam-core pipe, electric wire conduit, rigid shaped section, etc..
| Grade | PVC QS-1050P | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 1000-1100 | GB/T 5761,Appendix A | K value 66-68 | |
| Apparent density, g/ml | 0.51-0.57 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 21 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %,≥ | 80 | GB/T 15595-95 | ||
Grade QS-1200
Grade QS-1200 can be used to produce flexible film and sheet, rigid extrusion material, piping molding-die tool, pressed material, wire and cable insulating material, etc.
| Grade | PVC QS-1200 | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 1150-1250 | GB/T 5761,Appendix A | K value 69-71 | |
| Apparent density, g/ml | 0.47 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 25 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | ≥5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %,≥ | 80 | GB/T 15595-95 | ||
Grade QS-1350
Grade QS-1350 can be used to produce high-strength flexible products, pressed material, rigid or flexible extrusion section, and insulating material, etc..
| Grade | PVC QS-1350F | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 1300-1400 | GB/T 5761,Appendix A | K value 72-74 | |
| Apparent density, g/ml | 0.47 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 27 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %,≥ | 80 | GB/T 15595-95 | ||
| Water extracts conductivity, S/cm·g, ≤ | 5 | GB 2915-1999 | ||
Package
PVC resin is packed with compound bag of kraft paper and PP woven material, or internally coated PP woven cloth exterior bag with LDPE film-lined interior bag, or in bulk. The seal of packing bag should guarantee the products not to be polluted or leaked during normal transportation and storage. The net content of small package is 25kg per bag, while big package is 1250kg, 1000kg, 600k or 500kg.
(1) Packing : 25kg net/pp bag, or kraft paper bag .
(2) Loading quantity : 680Bags/20'container, 17MT/20'container .
(3) Loading quantity : 1000Bags/40'container, 25MT/40'container .
Manufacture introduction
Sinopec Qilu Petrochemical Corporation, located in Zibo city, Shandong province, with 24.8 square kilometers area, is a super-large refining, chemical, fertilizer and chemical fiber manufacturer integrated with petroleum, salt, coal, natural gas chemical process.
Over 40 years’ growth since 1966, Qilu has been equipped with facilities for 10.5 million tons refinery, 800 thousand tons ethylene, 1.1million tons synthetic resin, 450 thousand tons caustic soda, 300 thousand tons rubber, 450 thousand tons benzenes, 435 thousand tons alcohols, 480 thousand tons urea, and 500 thousand kilowatt cogeneration. There are over 120 grades of petrochemical products: gasoline, kerosene, diesel, PE, PP, PVC, synthetic rubber/fiber. Production of butanol/2-EH, SBR and PVC (ethylene method) is among the top ranks in China.
Recent years witnessed great effort by Qilu to build a state-own enterprise of high economic, political and social responsibilities through ways of resource conservation, environmental protection, energy saving and emission reduction under the guiding principle of scientific outlook on development and improving internal controls. By the end of 2011, Qilu has accumulatively processed 283 million tons of crude and produced 11.98 million tons ethylene. Qilu was listed among Top 100 enterprises for scientific and technological progresses, won “Golden Horse” award for enterprise management, Mayday Work Prize, Advanced Collective Unit for National Accounting Work, Advanced Collective for Comprehensive Utilization of National Resources, and Advanced Collective for Corporate Affairs Transparency and Excellence Unit for National Political Works.
The year 2011 saw Qilu’s success in achieving its promises of zero HSE accident and maximizing economic returns. The company set as a working theme “strengthening management for better performance” and as a working guidance “better production, systematic management, more training and enterprise harmony building”. It made steady progresses in the main product output throughout the year by refining 10.72 million tons of crude, producing 5.98 million tons oil products, 852 thousand tons of ethylene, 1.147 million tons of plastics, 460 thousand tons of caustic soda, 404 thousand tons of rubber, 331 thousand tons of butanol/2-EH, 63.5 thousand tons of acrylonitrile, 592 thousand of acrylic fiber and 3.86 billion kilowatt-hours cogeneration. Crude processing, oil products, rubber and acrylonitrile production hit a new record. Meanwhile, Qilu has become the biggest rubber producer in China.