Raw materials for preparing corrugated dual-wall hard PVC pipe
Raw materials for preparing corrugated dual-wall hard PVC pipe,
Raw material for produce corrugated dual-wall PVC pipe,
Polyvinyl Chloride (PVC) is a linear thermoplastic resin produced by polymerization of vinyl chloride monomer. Due to the differenceof raw materials, there are two methods of synthesizing vinyl chloride monomer calcium carbide process and petroleum process. Sinopec PVC adopts two suspension process, respectively from Japanese Shin-Etsu Chemical Company and American Oxy Vinyls Company. The product has good chemical corrosion resistance, excellent electrical insulation property and fine chemical stability. With high chlorine content, the material has good fire retardance and self-extinguishing properties. PVC is easy to process by extrusion, injection molding, calendering, blow molding, compressing, cast moulding and thermal molding, etc.
Application
PVC is one of the most widely used thermoplastic resins. It can be used to make products with high hardness and strength, such as pipes and fittings, profiled doors, windows and packaging sheets.
It can also make soft products, such as films, sheets, electrical wires and cables, floorboards and synthetic leather, by addition of plasticizers.
Parameters
| Grade | PVC QS-1050P | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 1000-1100 | GB/T 5761,Appendix A | K value 66-68 | |
| Apparent density, g/ml | 0.51-0.57 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 21 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10 minutes later), %,≥ | 80 | GB/T 15595-95 | ||
Raw material used for making hard corrugated PVC pipe is prepared from
PVC (100 pts.wt.),
trisalt (6.4-6.8 pts.wt.),
lead stearate (0.42-0.47 pts.wt.),
barium stearate (1.4-1.7 pts.wt.),
stearic acid (0.42-0.47 pts.wt.),
microcrystal paraffin (0.36-0.41 pts.wt.),
polyvinyl wax (0.58-0.62 pts.wt.),
ACR (401) (1.9-2.1 pts.wt.),
chlorinated polyethylene (5.8-6.3 pts.wt.),
superfine calcium carbonate (9-11 pts.wt.)
AC 316 (0.28-0.33 pts.wt.).
Its advantages are high lubricating performance, impact strength, ring rigidity and Vicat softening temp, good demoulding nature, and excellent low-temp plasticity.