PVC S-1300

short description:

Product Name: PVC Resin

Other Name: Polyvinyl Chloride Resin

Appearance: White Powder

K value: 71-73

Grades -Formosa ( Formolon) / Lg ls 100h / Reliance 6701 / Cgpc H66 / Opc S107 / Inovyn/ Finolex / Indonesia / Phillipine / Kaneka s10001t etc…

HS Code: 3904109001

 


Product Detail

Product Tags

PVC S-1300,
PVC for artifical leather, PVC resin for soft board, PVC resin for wire and cable, PVC S-1300,

Grade S-1300 is mainly used to produce high-strength flexible products, pressed materials, rigid and flexible extrusion molding and insulating materials, etc. Such as thin film, thin plate, artificial leather, wire, cable sheath and soft all kinds of profiles

Parameters

Grade PVC S-1300 Remarks
Item Guarantee value Test method
Average polymerization degree 1250-1350 GB/T 5761,Appendix A K value 71-73
Apparent density, g/ml 0.42-0.52 Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,           ≤ 0.30 Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,          ≥ 27 Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                         ≤ 5 GB/T 4615-1987
Screenings % 2.0  2.0 Method 1: GB/T 5761, Appendix B
Method 2: Q/SH3055.77-2006,
Appendix A
95  95
Fisheye number, No./400cm2,                        ≤ 20 Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,                ≤ 16 GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,      ≥ 78 GB/T 15595-95

PVC S-1300 ,1300 type PVC resin is mainly used in wire and cable,high strength film products ,artificial leather ,soft board/sheet ,plastic shoes and thermoplastic elastomer and other fields due to 1300 type PVC resin than general 1000 type PVC resin molecular quality high viscosity, so its in the processing process and mixing with It is different from the aspect

At present, most cable material manufacturers in order to improve product performance, have used higher degree of polymerization 1300 type PVC resin instead of the original use of 1000 type PVC resin, and even some manufacturers have begun to use higher degree of polymerization 1700 or even 2500 type PVC resin to produce higher performance of high-grade cable material.

PVC S-1300 is mainly used for the production of soft products.When the plasticizer to reduce the viscosity of PVC melt, processing temperature obviously down PVC melt flow change line and viscosity change and plasticizer varieties and dosings have a direct relationship.