pvc resin used in flooring
pvc resin used in flooring,
Polyvinyl chloride, PVC resin for siding and floor,
PVC flooring is produced from polyvinyl chloride material. Specifically, it is made of polyvinyl chloride and its copolymer resin as the main raw material, adding fillers, plasticizers, stabilizers, colorants and other auxiliary materials, on sheet continuous substrate, produced by coating process or rolling, extrusion or extrusion process, so it is a safe and environmentally friendly green material without formaldehyde.
The MAIN RAW MATERIAL THAT PVC FLOOR USES IS PVC MATERIAL AND CALCIUM CARBONATE, PVC MATERIAL AND CALCIUM CARBONATE ARE ENVIRONMENTAL PROTECTION AVIRULENT RENEWABLE RESOURCES, AVIRULENT, WITHOUT RADIATION. It has been widely used in People’s Daily life, such as water pipes, tableware, medical infusion bags, etc., is a green product strongly advocated by the country.
Because THIS NORMAL PVC FLOOR DOES NOT CONTAIN FORMALDEHYDE, BENZENE, PHENOL and other harmful chemicals, also DO not HAVE radioactivity.
PVC S-1000 polyvinyl chloride resin is produced by suspension polymerization process using vinyl chloride monomer as raw material. It is a kind of polymer compound with a relative density of 1.35 ~ 1.40. Its melting point is about 70 ~ 85℃. Poor thermal stability and light resistance, over 100℃ or long time under the sun hydrogen chloride begins to decompose, plastic manufacturing needs to add stabilizers. The product should be stored in a dry and ventilated warehouse. According to the amount of plasticizer, the plastic softness can be adjusted, and the paste resin can be obtained by emulsion polymerization.
Grade S-1000 can be used to produce soft film, sheet, synthetic leather, piping, shaped bar, bellow, cable protection piping, packing film, sole and other soft sundry goods.
Parameters
| Grade | PVC S-1000 | Remarks | ||
| Item | Guarantee value | Test method | ||
| Average polymerization degree | 970-1070 | GB/T 5761,Appendix A | K value 65-67 | |
| Apparent density, g/ml | 0.48-0.58 | Q/SH3055.77-2006, Appendix B | ||
| Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
| Plasticiser absorption of 100g resin, g, ≥ | 20 | Q/SH3055.77-2006, Appendix D | ||
| VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
| Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
| 95 | 95 | |||
| Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
| Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
| Whiteness (160ºC, 10minutes later), %, ≥ | 78 | GB/T 15595-95 | ||
Packaging
(1) Packing : 25kg net/pp bag, or kraft paper bag .
(2) Loading quantity : 680Bags/20′container, 17MT/20′container .
(3) Loading quantity : 1000Bags/40′container, 25MT/40′container .