PVC for soft film
PVC for soft film,
pvc for agricultural film,PVC Decorative Film raw material,Rigid PVC Film raw material,PVC for Transparent film,
PVC S-1000 polyvinyl chloride resin is produced by suspension polymerization process using vinyl chloride monomer as raw material. It is a kind of polymer compound with a relative density of 1.35 ~ 1.40. Its melting point is about 70 ~ 85℃. Poor thermal stability and light resistance, over 100℃ or long time under the sun hydrogen chloride begins to decompose, plastic manufacturing needs to add stabilizers. The product should be stored in a dry and ventilated warehouse. According to the amount of plasticizer, the plastic softness can be adjusted, and the paste resin can be obtained by emulsion polymerization.
Grade S-1000 can be used to produce soft film, sheet, synthetic leather, piping, shaped bar, bellow, cable protection piping, packing film, sole and other soft sundry goods.
Parameters
Grade | PVC S-1000 | Remarks | ||
Item | Guarantee value | Test method | ||
Average polymerization degree | 970-1070 | GB/T 5761,Appendix A | K value 65-67 | |
Apparent density, g/ml | 0.48-0.58 | Q/SH3055.77-2006, Appendix B | ||
Volatiles content (water included), %, ≤ | 0.30 | Q/SH3055.77-2006, Appendix C | ||
Plasticiser absorption of 100g resin, g, ≥ | 20 | Q/SH3055.77-2006, Appendix D | ||
VCM residue, mg/kg ≤ | 5 | GB/T 4615-1987 | ||
Screenings % | 2.0 | 2.0 | Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A |
|
95 | 95 | |||
Fisheye number, No./400cm2, ≤ | 20 | Q/SH3055.77-2006, Appendix E | ||
Number of impurity particles, No., ≤ | 16 | GB/T 9348-1988 | ||
Whiteness (160ºC, 10minutes later), %, ≥ | 78 | GB/T 15595-95 |
Packaging
(1) Packing : 25kg net/pp bag, or kraft paper bag .
(2) Loading quantity : 680Bags/20'container, 17MT/20'container .
(3) Loading quantity : 1000Bags/40'container, 25MT/40'container .
PVC shrink film is very common in the current packaging market, such as the outer packaging of cosmetics, stationery, doors and windows, aluminum and various stainless steel pipes. Because PVC shrinkage film has good shrinkage and strong tensile force, and the packaging is simple and easy to operate, it can be tightly fixed on the surface of the product only by heating with a high-power blower or semi-automatic and full-automatic heat shrinker